Jenis dan prinsip kerja plat gelongsor: Peranti muncung gelongsor terdiri daripada plat gelongsor atas dan bawah yang diperbuat daripada bahan refraktori dan struktur pemanduan mekanikal, dan dipasang di luar bahagian bawah senduk. Plat gelongsor atas dibetulkan dan plat gelongsor bawah boleh digerakkan. Mengikut mod tindakan plat pintu slaid refraktori, ia boleh dibahagikan kepada tiga kategori: 1) Jenis salingan linear: 2) Jenis mendorong linear: 3) Jenis berputar. Dengan memacu rod tarik, plat pintu gelongsor refraktori meluncur ke depan dan ke belakang dalam garis lurus. Apabila lubang tuangan pada bata plat pintu slaid atas dan bawah refraktori berperingkat, lubang muncung atas dipenuhi dengan pasir saliran, dan senduk keluli boleh dimuatkan dengan keluli; apabila lubang tuangan bertindih, pasir saliran mengalir keluar secara automatik, dan kemudian Menuang, dan kelajuan menuang boleh dikawal oleh tahap pertindihan lubang tuangan.

Plat gelongsor adalah komponen utama yang menentukan fungsi muncung gelongsor dan memainkan peranan dalam mengawal dan mengawal aliran keluli cair. Disebabkan oleh sentuhan berulang pada plat gelongsor dengan -suhu tinggi keluli cair (terutamanya bahagian lubang tuangan), kakisan adalah serius dan keadaan penggunaannya adalah keras. Plat pintu slaid refraktori dikehendaki mempunyai sifat yang baik seperti kekuatan tinggi, rintangan kakisan, dan rintangan mengelupas. Semasa proses menuang, ia dipastikan bahawa keluli cair tidak boleh bocor di antara plat pintu gelongsor refraktori. Plat pintu gelangsar refraktori mesti mempunyai sifat berikut

(1) Kerataan permukaan gelongsor<0.05mm

(2) Kekuatan mekanikal yang tinggi

(3) Rintangan kuat terhadap hakisan oleh keluli cair dan sanga cair;

(4) Sifat antioksidan yang sangat baik

(5) Kestabilan kejutan haba yang baik.

Perlindungan pengedap muncung gelongsor senduk adalah terutamanya pada sambungan antara muncung atas dan plat slaid atas, dan plat slaid bawah dan muncung bawah. Semasa proses menuang, secara amnya selepas menuang satu atau dua relau keluli cair, plat slaid bawah dan alur keluar longkang mesti diganti dan dipasang semula. Perlindungan pengedap menggunakan gentian atau pad pengedap tanah liat untuk memastikan kebersihan tinggi keluli cair dan keseragaman kualiti dalaman papak tuang.

terbakar ke dalam plat pintu gelongsor refraktori

Dalam plat gelongsor karbon aluminium yang dibakar, bukan sahaja pengikat organik dikarbonkan dan dikok semasa pembakaran, membentuk ikatan karbon dalam bata, tetapi juga bahan tambahan, seperti silikon logam, boleh bergabung dengan karbon untuk membentuk Sic apabila dikurangkan dan dibakar pada<1300°C. , and a ceramic bond is formed within the brick body. Therefore, there is a dual bonding system of ceramic bonding and carbon bonding in the fired aluminum carbon sliding plate. It significantly improves the strength of the refractories slide gate plate, and even after the carbon is burned out during use, it can maintain sufficient residual strength because it is a ceramic bonding system. After the refractories slide gate plate is burned, it is usually soaked in oil. Vertical or horizontal vacuum-pressurized oil immersion devices are generally used in oil immersion. After the slide is preheated, put it into the oil immersion tank, and evacuate it to a vacuum℃of 650mmHg or above, introduce heated tar or asphalt, and pressurize the oil to 8~16kgf/cm2 or higher to make the tar or asphalt Being sucked into the open air holes of the refractories slide gate plate. The cast holes in the refractories slide gate plate can be made during molding, or they can be formed into a whole plate without holes and then drilled later. Most people think that drilling is beneficial to improve the quality of the refractories slide gate plate. In addition, wrapping and hooping the refractories slide gate plate with thin iron sheets is considered an important measure to ensure the safe use of the refractories slide gate plate. It can prevent the refractories slide gate plate from breaking during use, and because this metal hoop is wrapped very tightly, it has limitations. The propagation of cracks in materials, especially the effect of crack opening.

Plat pintu slaid refraktori berprestasi tinggi

Ia ialah plat pintu gelongsor refraktori karbon aluminium yang tidak terbakar dengan proses yang agak mudah, kos rendah dan kesan penggunaan yang baik. Bahan-bahan plat pintu gelongsor refraktori jenis ini adalah serupa dengan bahan plat pintu gelongsor refraktori yang dipecat. Ia menggunakan bahan mentah seperti korundum, mullite, korundum, grafit serpihan, silikon karbida dan serbuk silikon, dan menambah resin fenolik sebagai pengikat. Selepas pencampuran, pengacuan, rawatan haba dan pemprosesan mekanikal Itulah produk siap. Berbanding dengan plat pintu slaid refraktori karbon aluminium yang dibakar, plat pintu slaid refraktori yang tidak terbakar tidak memerlukan penembakan, rendaman minyak dan rawatan haba retort semasa pembuatan, yang memudahkan proses pengeluaran, tetapi kekuatannya lebih rendah dan keliangannya lebih tinggi sedikit. Amalan telah membuktikan bahawa plat gelongsor yang tidak-terbakar mempunyai kesan yang baik apabila digunakan pada sudu penukar bersaiz sederhana-dan relau elektrik, malah ada juga yang mengatasi plat gelongsor terendam minyak-yang terbakar.

Cara memasang dan menggunakan plat pintu slaid refraktori

Jumlah dan kekerasan tanah liat api di antara plat gelongsor dan muncung hendaklah sesuai untuk menjadikan sambungan seragam dan kekuatan yang sesuai untuk meningkatkan-kadar bukaan sendiri muncung, mengelakkan pembakaran oksigen dan saliran, mengurangkan pengoksidaan plat gelongsor dan pengembangan lubang untuk mengelakkan muncung daripada "berpusing" apabila keluli cair dituangkan. Kejadian fenomena "slagging" perlu dikurangkan bagi mengurangkan hakisan sanga pada permukaan plat gelongsor. Apabila mengawal aliran keluli tuangan berterusan dan menutup operasi selepas menuang, lejang 1 harus diselamatkan dengan meniup oksigen untuk mengeluarkan keluli sisa dan mengelakkan keluli sisa daripada dikendalikan dengan tidak betul dan menyebabkan pengembangan berlebihan plat gelongsor.